2018 | AFC ACCOMPLISHMENTS 151 effort between LANL, University of California Santa Barbara (UCSB) and Oak Ridge National Laboratory (ORNL) named FCRD-NFA1. Significant progress has been made at processing this alloy into tube form. Through a bilateral collaboration with Centrale Energie Atomique (CEA), pilger processing was used to produce a 915 mm long tube with a 10.73 mm OD and wall thickness of 0.5 mm (Figure 2). In addition, tubing was produced at Case Western Reserve University Figure 1. Transmission Electron Microscopy (TEM) micrographs of low and high nitrogen Fe-12Cr-0.2C alloys after ion irradiation to 0.5 and 1.0 dpa using protons.