Page 1 Page 2 Page 3 Page 4 Page 5 Page 6 Page 7 Page 8 Page 9 Page 10 Page 11 Page 12 Page 13 Page 14 Page 15 Page 16 Page 17 Page 18 Page 19 Page 20 Page 21 Page 22 Page 23 Page 24 Page 25 Page 26 Page 27 Page 28 Page 29 Page 30 Page 31 Page 32 Page 33 Page 34 Page 35 Page 36 Page 37 Page 38 Page 39 Page 40 Page 41 Page 42 Page 43 Page 44 Page 45 Page 46 Page 47 Page 48 Page 49 Page 50 Page 51 Page 52 Page 53 Page 54 Page 55 Page 56 Page 57 Page 58 Page 59 Page 60 Page 61 Page 62 Page 63 Page 64 Page 65 Page 66 Page 67 Page 68 Page 69 Page 70 Page 71 Page 72 Page 73 Page 74 Page 75 Page 76 Page 77 Page 78 Page 79 Page 80 Page 81 Page 82 Page 83 Page 84 Page 85 Page 86 Page 87 Page 88 Page 89 Page 90 Page 91 Page 92 Page 93 Page 94 Page 95 Page 96 Page 97 Page 98 Page 99 Page 100 Page 101 Page 102 Page 103 Page 104 Page 105 Page 106 Page 107 Page 108 Page 109 Page 110 Page 111 Page 112 Page 113 Page 114 Page 115 Page 116 Page 117 Page 118 Page 119 Page 120 Page 121 Page 122 Page 123 Page 124 Page 125 Page 126 Page 127 Page 128 Page 129 Page 130 Page 131 Page 132 Page 133 Page 134 Page 135 Page 136 Page 137 Page 138 Page 139 Page 140 Page 141 Page 142 Page 143 Page 144 Page 145 Page 146 Page 147 Page 148 Page 149 Page 150 Page 151 Page 152 Page 153 Page 154 Page 155 Page 156 Page 157 Page 158 Page 159 Page 160 Page 161 Page 162 Page 163 Page 164 Page 165 Page 166 Page 167 Page 168 Page 169 Page 170 Page 171 Page 172 Page 173 Page 174 Page 175 Page 176 Page 177 Page 178 Page 179 Page 180 Page 181 Page 182 Page 183 Page 184 Page 185 Page 186 Page 187 Page 188 Page 189 Page 190 Page 191 Page 192 Page 193 Page 194 Page 195 Page 196 Page 197 Page 198 Page 199 Page 200 Page 201 Page 202 Page 203 Page 204 Page 205 Page 206 Page 207 Page 208 Page 209 Page 210 Page 211 Page 212 Page 213 Page 214 Page 215 Page 216 Page 217 Page 218 Page 219 Page 220 Page 221 Page 222 Page 223 Page 224 Page 225 Page 226 Page 227 Page 228 Page 229 Page 230 Page 231 Page 232 Page 233 Page 234 Page 235 Page 236 Page 237 Page 238 Page 239 Page 240 Page 241 Page 2422016 | AFC ACCOMPLISHMENTS 74 TheATF-1, LANL-1 irradiation test in theAdvancedTest Reactor (ATR) consists of Kanthal (FeCrAl)-clad U3Si5 and UN-U3Si5 fuels. This fuel-clad system was selected after initial screening evaluations consisting of fuel-material reaction couples, thermophysical property measurements, themodynamic analysis, and neutronic performance and safety calculations of several composite fuel concepts. Project Description The nominal irradiation-test parameters are shown inTable 1 where highest priority was placed on understanding the relationship between fuel phase enrichment, fuel-centerline temperature, and burnup (BU) for a fixed, linear heat-generation rate (LHGR).The 235 U enrichments for the two fuel phases in the first three rodlets were chosen so that the 235 U atoms/cm3 would be the same across the composite. For these rodlets, the volumetric heat generation should be approximately the same across the pellet, whereas the damage accumu- lation in the U3Si5 should be greater than in the UN.The fuel-centerline tempera- tures for rodlets 1 and 2 are 1000°C and 700°C, respectively, with a target BU of 10 GWd/MTU. Rodlet 3 is a 700°C test with BU extended to 20 GWd/MTU. Rodlet 4 is a U3Si5 fuel test, with no UN. While monolithic U3Si5 is not being advocated as a standalone fuel concept due to the relatively low uranium density of 7.5 g/cm3, the silicide-only rodlet is being irradiated as an efficient way to collect irradiation-behavior data for this composite constituent phase. The fuel phases in Rodlet 5 will have the same 235 U enrichment.As a result, the UN should have a greater heat flux and more radiation damage than the U3Si5 phase.This rodlet will be tested at 700°C to 10 GWd/MTU BU for comparison with Rodlet 2. Previously determined feedstock- synthesis routes and processing parameters were adopted for use in the fabrication campaign to produce fuel forATR irradiation.The process to fabricate UN- U3Si5 and U3Si5 fuel can be generally divided into three steps: (1) feedstock synthesis, (2) pellet fabrica- tion, and (3) pellet characterization. Depleted and low-enriched uranium nitride feedstock was produced using the historical carbothermic-reduction nitridization process developed in the 1980s at LosAlamos National Labora- tory (LANL) and optimized for this fuels campaign. Milled and sieved depleted- UN powder was shown to be phase- pure, as indicated by X-ray diffraction (XRD), and combustion analysis produced oxygen and carbon results of 426 ppm and 237 ppm, respectively. XRD of low-enriched UN powder indi- cated trace amounts of impurity UO2 . XRD of the depleted and low-enriched Fabrication of U3Si5 and UN/U3Si5 Fuels for the LANL-1/ATF-1 Test Principal Investigators: S.L.Voit, K.J. McClellan, J.T.White, D.D. Byler, E.P. Luther Table 1. ATF-1/LANL-1 nominal test design parameters.